홈 > 제품정보 >
- Product Sturcture
- Product Line up
-
HISTORY ITEM NTN HFP HSI NTA NTH TEST METHOD Tensile Strength gf/mm MD 3000↑ Sample Size:12.65㎜(Width) x 160㎜(Length)
Elongation Speed : 100mm/min
Measure Average load and length
Elongation＝Length Gap ｘ 100(％) 60↑ ITEM Tensile Strength gf/mm MD 3000↑
Elongation% MD 60↑ Sample Size:12.65㎜(Width) x 160㎜(Length)
Elongation Speed : 100mm/min
Measure Average load and length
Elongation＝Length Gap ｘ 100(％)Heat Shrinkage % MD 3.0↓ Sample Size : 120㎜(Width) x 120㎜(Length)
Oven Temperature : 150℃ x 30min
Measure after 30 min in room temperature
Measurement Equpment : Optcal Microscope ( x 100)(Reference : JISS-7133 /ASTM D204)TD 1.0↓ Bonding Strength ofFilm : Film gf/cm 160±10℃ 800↑ 400↑ 500↑ 2000↑ 800↓ Method：Heat Seal Test Machine.
Lamination roll speed : 100㎜/min
Lamination Heating Temperature:160±10℃Pressure:3.0kg/㎠
Pressure time : 1.0 secPeel off Speed : 50±5㎜/min
Peel Angle : T-shapeBonding Strength ofFilm : Conductor gf/mm 160±10℃ 50↑ 40↑ 50↑ 40↑ 50↑
Lamination roll speed :100㎜/min
Lamination Heating Temperature : 160±10℃
Pressure : 3.0kg/㎠Peel off Speed : 50±5㎜/min
Peel Angle : T-shapeFlammability PASS PASS PASS PASS PASS Sample Size : 50㎜(Width) x 200㎜(Length)Burning Test.Sample Setting : Set in φ12.7±0.5Open at lower 125mm
Flame length : 20㎜Ignition : touch flame for 3 seconds apart below 10mm,re touch flame for 3 seonds
Measure time after flame go off.UL80℃ equivalent 80℃ PASS PASS PASS PASS PASS Method:Roll laminate Machine
laminate Speed：2.0m/min.Pressure：0.3MPa
Sample：「Z fold」
Condition：113℃×1Week、UL105℃ equivalent 105℃ PASS PASS PASS PASS PASS VW-1 equivalent PASS PASS PASS PASS PASS COSMO Method